Metals - Ferrous ScrapMetals - Ferrous Scrap » Cast Iron Grades252 - Cupola CastClean cast iron scrap such as columns, pipes, plates, and castings of a miscellaneous nature, including automobile blocks and cast iron parts of agricultural and other machinery. Free from stove plate, burnt iron, brake shoes or foreign material. Cupola size, not over 24 inches x 30 inches, and no piece over 150 pounds in weight. 253
- Charging Box Cast
Clean
cast iron scrap in sizes not over 60 inches in length or 30 inches in width,
suitable for charging into an open hearth furnace without further preparation.
Free from burnt iron, brake shoes, or stove plate. 254
- Heavy Breakable Cast
Cast
iron scrap over charging box size or weighing more than 500 pounds. May
include cylinders and driving wheel centers. May include steel which does not
exceed 10 percent of the casting by weight. 255
- Hammer Block Or Bases
Cast
iron hammer blocks or bases. 256
- Burnt Iron
Burnt
cast iron scrap, such as stove parts, grate bars, and miscellaneous burnt
iron. May include sash weights or window weights. 257
- Mixed Cast
May
include all grades of cast iron except burnt iron. Dimensions not over 24
inches x 30 inches and no piece over 150 pounds in weight. 258
- Stove Plate, Clean Cast Iron Stove
Free
from malleable and steel parts, window weights, plow points, or burnt cast
iron. 259
- Clean Auto Cast.
Clean
auto blocks; free of all steel parts except camshafts, valves, valve springs,
and studs. Free of nonferrous and
non-metallic parts. 260 - Unstripped Motor
Blocks
Automobile
or truck motors from which steel and nonferrous fittings may or may not have
been removed. Free from driveshafts and all parts of frames. 261
- Drop Broken Machinery Cast.
Clean
heavy cast iron machinery scrap that has been broken under a drop. All pieces
must be of cupola size, not over 24 inches x 30 inches, and no piece over 150
pounds in weight. 262
- Clean Auto Cast, Broken, Not Degreased.
Clean
auto blocks, free of all steel parts except camshafts, valves, valve springs
and studs. Free of nonferrous and non-metallic parts, and must be broken to
cupola size, 150 pounds or less. 263
- Clean Auto Cast, Degreased.
Free
of all steel parts except camshafts, valves, valve springs, and studs. Free of
nonferrous and non-metallic parts, and must be broken into cupola size, 150
pounds or less. 264
- Malleable.
Malleable
parts of automobiles, railroad cars, locomotives, or miscellaneous malleable
iron castings. Free from cast iron and steel parts and other foreign material. 265
- Broken Ingot Molds And Stools
Broken
ingot molds and stools, cast iron, maximum size 2 feet x 3 feet x 5 feet. 266
- Unbroken Ingot Molds And Stools.
Unbroken
ingot molds and stools, cast iron. Metals - Ferrous Scrap » Electric Furnace Casting And Foundry Grades
229
- Billet, Bloom And Forge Crops
Billet,
bloom, axle, slab, heavy plate and heavy forge crops, containing not over 0.05
percent phosphorus or sulphur and not over 0.5 percent silicon, free from
alloys. Dimensions not less than 2 inches in thickness, not over 18 inches in
width, and not over 36 inches in length. 230
- Bar Crops And Plate Scrap
Bar
crops, plate scrap, forgings, bits, jars, and tool joints, containing not over
0.05 percent phosphorus or sulphur, not over 0.5 percent silicon, free from
alloys. Dimensions not less than 1/2 inch in thickness, not over 18 inches in
width, and not over 36 inches in length. 231
- Plate And Structural Steel, 5 Feet And Under
Cut
structural and plate scrap, 5 feet and under. Clean open hearth steel plates,
structural shapes, crop ends, shearings, or broken steel tires. Dimensions not
less than 1/4 inch thickness, not over 5 feet in length and 18 inches in
width. Phosphorus or sulphur not over 0.05 percent. 232
- Plate And Structural Steel, 5 Feet And Under
Cut
structural and plate scrap, 5 feet and under. Clean open hearth steel plates,
structural shapes, crop ends, shearings, or broken steel tires. Dimensions not
less than 1/4 inch thickness, not over 5 feet in length and 24 inches in
width. Phosphorus or sulphur not over 0.05 percent. 233
- Cast Steel
Steel
castings not over 48 inches long or 18 inches wide, and 1/4 inch and over in
thickness, containing Institute of Guidelines for Ferrous Scrap Scrap
Recycling Industries, Inc. 17 Co d e I t em Co d e I t em not over 0.05
percent phosphorus or sulphur, free from alloys and attachments. May include
heads, gates, and risers. 234
- Punchings And Plate Scrap
Punchings
or stampings, plate scrap, and bar crops containing not over 0.05 percent
phosphorous or sulphur and not over 0.5 percent silicon, free from alloys. All
materials cut 12 inches and under, and with the exception of punchings or
stampings, at least 1/8 inch in thickness. Punchings or stampings under 6
inches in diameter may be any gauge. 235
- Electric Furnace Bundles
New
black steel sheet scrap hydraulically compressed into bundles of size and
weight as specified by consumer. 236
- Cut Structural And Plate Scrap, 3 Feet And Under.
Clean
open hearth steel plates, structural shapes, crop ends, shearings, or broken
steel tires. Dimensions not less than 1/4 inch in thickness, not over 3 feet
in length and 18 inches in width. Phosphorus or sulphur not over 0.05 percent. 237
- Cut Structural And Plate Scrap, 2 Feet And Under.
Same
as cut structural and plate scrap, 3 feet and under, except for length. 238
- Cut Structural And Plate Scrap, 1 Foot And Under.
Same
as cut structural and plate scrap, 3 feet and under, except for length. 239
- Silicon Busheling
Clean
silicon bearing steel scrap, not exceeding 12 inches in any dimension,
including new factory busheling (for example, sheet clippings, stampings,
etc.), having a silicon content of 0.05 percent to 5.0 percent. 240
- Silicon Clippings
Clean
steel scrap, including new factory busheling (for example, sheet clippings,
stampings, etc.), may not include old auto body and fender stock. Free of
metal coated, limed, vitreous enameled, and electrical sheet containing
minimum 1 percent silicon. 241
- Chargeable Ingots And Ingot Butts.
Chargeable
ingots and ingot butts for material to be suitable and acceptable to the
consumer containing not over 0.05 percent phosphorus or sulphur and not over
0.05 percent silicon free of alloys. 242
- Foundry Steel, 2 Feet And Under
Steel
scrap 1/8 inch and over in thickness, not over 2 feet in length or 18 inches
in width. Individual pieces free from attachments. May not include nonferrous
metals, cast or malleable iron, cable, vitreous enameled, or metal coated
material. 243
- Foundry Steel, 1 Foot And Under
Same
specifications as 2-foot material, except for length. 243A
- Low Residual, Black Foundry Busheling
1000
series black carbon steel scrap, 1/8 inch and over in thickness, not more than
12 inch x 24 inch, manganese content not more than 0.50 percent. Other
parameters subject to agreement between supplier and consumer 243B
- Low Residual, Ductile Quality Shredded Clips
Shredded
black 1000 series carbon steel scrap, 1/8 inch and over in thickness, minimum
average density of 75 PCF, manganese content not more than 0.50 percent. Other
parameters subject to agreement between supplier and consumer. 244
- Springs And Crankshafts
Clean
automotive springs and crankshafts, either new or used. 245
- Alloy Free Turnings
Clean
shoveling steel turnings free from lumps, tangled or matted material, iron
borings, or excessive oil containing not more than 0.05 percent phosphorus or
sulphur, and free of alloys. 246
- Alloy Free Short Shoveling Steel Turnings
Clean
shoveling steel turnings, free of lumps, tangled or matted material, iron
borings, or excessive oil, containing not more than 0.05 percent phosphorus or
sulphur, and free of alloys. 247
- Alloy Free Machine Shop Turnings
Clean
steel turnings, free of iron borings or excessive oil, containing not more
than 0.05 percent phosphorus or sulphur, and free of alloys. May not include
badly rusted or corroded stock. 248
- Hard Steel Cut 30 Inches And Under
Automotive
steel consisting of rear ends, crankshafts, driveshafts, front axles, springs,
and gears prepared 30 inches and under. May not include miscellaneous small
shoveling steel or any pieces too bulky for gray iron foundry use. 249
- Chargeable Slab Crops
Chargeable
slab crops for material to be suitable and acceptable to the consumer
containing not over 0.05 percent phosphorus and 0.05 percent sulphur and not
over 0.05 percent silicon and free of alloys. 250
- Silicon Bundles
Silicon
sheet scrap, clippings or skeleton scrap, compressed or hand bundled, to
charging box size, and weighing not less than 75 pounds per cubic foot, having
a silicon content of 0.50 percent to 5.0 percent. 251
- Heavy Turnings.
Short,
heavy steel turnings, containing not over 0.05 percent phosphorus or sulphur
and free of alloys. May include rail chips. May not include machine shop or
other light turnings and must weigh not less than 75 pounds per cubic foot in
the original state of production. Metals - Ferrous Scrap » Other
200
- No. 1 Heavy Melting Steel
Wrought
iron and/or steel scrap 1/4 inch and over in thickness. Individual pieces not
over 60 x 24 inches (charging box size) prepared in a manner to insure compact
charging. 201
- No. 1 Heavy Melting Steel 3 Feet X 18 Inches
Wrought
iron and/or steel scrap 1/4 inch and over in thickness. Individual pieces not
over 36 x 18 inches (charging box size) prepared in a manner to insure compact
charging. 202
- No. 1 Heavy Melting Steel 5 Feet X 18 Inches.
Wrought
iron and/or steel scrap 1/4 inch and over in thickness. Individual pieces not
over 60 x 18 inches (charging box size) prepared in a manner to insure compact
charging. 203
- No. 2 Heavy Melting Steel
Wrought
iron and steel scrap, black and galvanized, 1/8 inch and over in thickness,
charging box size to include material not suitable as No. 1 heavy melting
steel. Prepared in a manner to insure compact charging. 204
- No. 2 Heavy Melting Steel
Wrought
iron and steel scrap, black and galvanized, maximum size 36 x 18 inches. May
include all automobile scrap properly prepared. 205
- No. 2 Heavy Melting Steel 3 Feet X 18 Inches
Wrought
iron and steel scrap, black and galvanized, maximum size 36 x 18 inches. May
include automobile scrap, properly prepared; however, to be free of sheet iron
or thin gauged material. 206
- No. 2 Heavy Melting Steel 5 Feet X 18 Inches
Wrought
iron and steel scrap, black and galvanized, maximum size 60 x 18 inches. May
include automobile scrap, properly prepared; however, to be free of sheet iron
or thin gauged material. 207
- No. 1 Busheling
Clean
steel scrap, not exceeding 12 inches in any dimensions, including new factory
busheling (for example, sheet clippings, stampings, etc.). May not include old
auto body and fender stock. Free of metal coated, limed, vitreous enameled,
and electrical sheet containing over 0.5 percent silicon. 207A
- New Black Sheet Clippings
For
direct charging, maximum size 8 feet by 18 inches, free of old automobile body
and fender stock, metal coated, lined, vitreous enameled and electrical sheet
containing over 0.5 percent silicon. Must lay reasonably flat in car. 208
- No. 1 Bundles
New
black steel sheet scrap, clippings or skeleton scrap, compressed or hand
bundled, to charging box size, and weighing not less than 75 pounds per cubic
foot. (Hand bundles are tightly secured for handling with a magnet.) May
include Stanley balls or mandrel wound bundles or skeleton reels, tightly
secured. May include chemically detinned material. May not include old auto
body or fender stock. Free of metal coated, limed, vitreous enameled, and
electrical sheet containing over 0.5 percent silicon. 209
- No. 2 Bundles
Old
black and galvanized steel sheet scrap, hydraulically compressed to charging
box size and weighing not less than 75 pounds per cubic foot. May not include
tin or lead-coated material or vitreous enameled material. 210
- Shredded Scrap
Homogeneous
iron and steel scrap, magnetically separated, originating from automobiles,
unprepared No. 1 and No. 2 steel, miscellaneous baling and sheet scrap.
Average density 50 pounds per cubic foot. 211
- Shredded Scrap
Homogeneous
iron and steel scrap magnetically separated, originating from automobiles,
unprepared No. 1 and No. 2 steel, miscellaneous baling and sheet scrap.
Average density 70 pounds per cubic foot. 212
- Shredded Clippings
Shredded
1000 series carbon steel clippings or sheets. Material should have an average
density of 60 pounds per cubic foot. 213
- Steel Can Bundles
Steel
can scrap compressed to charging box size and weighing not less than 75 pounds
per cubic foot. Cans may be baled without removal of paper labels, but free of
other non-metallics. May include up to 5 gallon tin coated containers. 214
- No. 3 Bundles
Old
sheet steel, compressed to charging box size and weighing not less than 75
pounds per cubic foot. May include all coated ferrous scrap not suitable for
inclusion in No. 2 bundles. 215
- Incinerator Bundles
Tin
can scrap, compressed to charging box size and weighing not less than 75
pounds per cubic foot. Processed through a recognized garbage incinerator. 216
- Terne Plate Bundles.
New
terne plate sheet scrap, clippings or skeleton scrap, compressed or hand
bundled, to charging box size, and weighing not less than 75 pounds per cubic
foot. (Hand bundles are tightly secured for handling with a magnet.) May
include Stanley balls or mandrel wound bundles or skeleton reels, tightly
secured. 217
- Bundled No. 1 Steel
Wrought
iron and/or steel scrap 1/8 inch or over in thickness, compressed to charging
box size and weighing not less than 75 pounds per cubic foot. Free of all
metal-coated material. 218
- Bundled No. 2 Steel
Wrought
iron or steel scrap, black or galvanized, 1/8 inch and over in thickness,
compressed to charging box size and weighing not less than 75 pounds per cubic
foot. Auto body and fender stock, burnt or hand stripped, may constitute a
maximum of 60 percent by weight. (This percent based on makeup of auto body,
chassis, driveshafts, and bumpers.) Free of all coated material, except as
found on automobiles. 219
- Machine Shop Turnings
Clean
steel or wrought iron turnings, free of iron borings, nonferrous metals in a
free state, scale, or excessive oil. May not include badly rusted or corroded
stock. 220
- Machine Shop Turnings And Iron Borings
Same
as machine shop turnings but including iron borings. 221
- Shoveling Turnings
Clean
short steel or wrought iron turnings, drillings, or screw cuttings. May
include any such material whether resulting from crushing, raking, or other
processes. Free of springy, bushy, tangled or matted material, lumps, iron
borings, nonferrous metals in a free state, grindings, or excessive oil. 222
- Shoveling Turnings And Iron Borings
Same
as shoveling turnings, but including iron borings. 223
- Iron Borings
Clean
cast iron or malleable iron borings and drillings, free of steel turnings,
scale, lumps or excessive oil. 224
- Auto Slabs
Clean
automobile slabs, cut 3 feet x 18 inches and under. 225
- Auto Slabs
Clean
automobile slabs, cut 2 feet x 18 inches and under. 226
- Briquetted Iron Borings
Analysis
and density to consumer’s specifications. 227
- Briquetted Steel Turnings.
Analysis
and density to consumer’s specifications. 228
- Mill Scale
Dark
colored, ranging from blue to black, ferromagnetic iron oxide forming on the
surface of steel articles during heating and working. Metals - Ferrous Scrap » Railroad Ferrous Scrap
(2)
- Axles, Steel
Solid
car and/or locomotive friction bearing, 8 inch diameter and under (free of
axles with key-way between wheel seats, no axles of shorter lengths than
distance between wheel seats to be included). (2A)
- Axles, Steel
Solid
car and/or locomotive friction bearing over 8 inch diameter (free of axles
with key-way between wheel seats, no axles of shorter length than distance
between wheel seats to be included). (3)
- Axles, Steel
Roller
bearing 8 inch diameter and under (no axles of shorter lengths than distance
between wheel seats to be included). (3A)
- Axles, Steel
Roller
bearing over 8 inch diameter (no axles of shorter length than distance between
wheel seats to be included). (4)
- Spikes, Track Bolts And Nuts, And Lock Washers, May Include Rail Anchors
(5)
- Tie Plates
Steel (6)
- Rail Joints, Angle And/Or Splice Bars
Steel. (9)
- Bolsters And/Or Truck Sides, Frames: Uncut.
Cast
steel. (11)
- Cast Steel, No. 2.
Steel
castings, over 18 inches wide and/or over 5 feet long. (11A)
- Cast Steel, No. 1
Steel
castings, 18 inches and under, not over 5 feet long, including cut truck side
frames and bolsters (12)
- Cast Iron, No. 1
Cast
iron scrap, such as columns, pipes, plates, and/ or castings of miscellaneous
nature, but free from stove plates, brake shoes, and burnt scrap. Must be
cupola size, not over 24 x 30 inches in dimension and no piece to weigh over
150 pounds. Must be free from foreign material. (13)
- Cast Iron, No. 2
Pieces
weighing over 150 pounds, but not more than 500 pounds. Free from burnt cast. (14)
- Cast Iron, No. 3
Pieces
weighing over 500 pounds; includes cylinders, driving wheel centers and/or all
other castings. (Free from hammer blocks or bases.) (15)
- Cast Iron, No. 4.
Burnt
cast iron scrap, such as grate bars, stove parts and/or miscellaneous burnt
scrap. (15)
- Cast Iron, No. 4
Burnt
cast iron scrap, such as grate bars, stove parts and/or miscellaneous burnt
scrap. (16)
- Cast Iron Brake Shoes
Brakes
shoes of all types except composition-filled shoes. (17)
- Couplers And/Or Knuckles
Railroad
car and/or locomotive steel couplers, knuckles and/or locks stripped clean of
all other attachments. (18)
- Frogs And/Or Switches, Uncut
Steel
frogs and switches that have not been cut apart, exclusive of manganese. (18A)
- Railbound Manganese Frogs And Switch Points With Manganese Inserts That Have
Not Been Cut Apart
(23)
- Malleable
Malleable
parts of automobiles, railroad cars, locomotive and/or miscellaneous malleable
castings. (24)
- Melting Steel, Railroad No. 1
Clean
wrought iron or steel scrap, 1/4 inch and over in thickness, not over 18
inches in width, and not over 5 feet in length. May include pipe ends and
material 1/8 inch to 1/4 inch in thickness, not over 15 inches x 15 inches.
Individual pieces cut so as to lie reasonably flat in charging box. (27)
- Rail, Steel No. 1
Standard
section tee rails, original weight 50 pounds per yard or heavier, 10 feet long
and over. Suitable for rerolling into bars and shapes. Free from bent and
twisted rails, frog, switch, and guard rails, or rails with split heads and
broken flanges. Continuous welded rail may be included provided no weld is
over 9 inches from the end of the piece of rail. (28A)
- Rail, Steel No. 2 Cropped Rail Ends
Standard
section, original weight of 50 pounds per yard and over, 18 inches long and
under. (28B)
- Rail, Steel No. 2 Cropped Rail Ends
Standard
section, original weight of 50 pounds per yard and over, 2 feet long and
under. (28C)
- Rail, Steel No. 2 Cropped Rail Ends
Standard
section, original weight 50 pounds per yard and over, 3 feet long and under. (29)
- Rail, Steel No. 3
Standard
section tee, girder, and/or guard rails, to be free from frog and switch rails
not cut apart, and contain no manganese, cast, welds, or attachments of any
kind except angle bars. Free from concrete, dirt, and foreign material of any
kind. (30)
- Sheet Scrap, No. 1
Under
3/16 inch thick, may include hoops, band iron and/or steel, scoops and/or
shovels (free of wood). Must be free from burnt or metal coated material,
cushion, or other similar springs. (31)
- Sheet Scrap, No. 2
Galvanized
or tinned material and/or gas retorts, and/or any other iron or steel material
not otherwise classified. (32)
- Steel, Tool
(Specify
kind in offering.) (33)
- Steel, Manganese
All
kinds of manganese, rail, guard rails, frogs and/or switch points, cut or
uncut. (34)
- Steel, Spring.
Coil
and/or elliptical, minimum thickness 1/4 inch, may be assembled or cut apart. (34A)
- Steel, Spring
Coil
only. (35)
- Structural, Wrought Iron And/Or Steel Uncut
All
steel or steel mixed with iron from bridges, structures and/or equipment that
has not been cut apart, may include uncut bolsters, brakebeams, steel trucks,
underframes, channel bars, steel bridge plates, frog and/or crossing plates
and/or other steel of similar character. (36)
- Tires
All
locomotive, not cut to specified lengths. (38)
- Turnings. No. 1
Heavy
turnings from wrought iron and/or steel railroad axles or heavy forgings
and/or rail chips, to weigh not less than 75 pounds per cubic foot. Free from
dirt or other foreign material of any kind. Alloy steel scrap may be excluded
from these specifications by mutual agreement between buyer and seller. (38A)
- Turnings, Drillings And/Or Borings. No. 2
Cast,
wrought, steel and/or malleable iron borings, turnings and/or drillings mixed
with other metals. (40)
- Wheels, No. 1
Cast
iron car wheels. (42)
- Wheels, No. 3
Solid
cast steel, forged, pressed and/or rolled steel car and/or locomotive wheels,
not over 42 inches diameter. (Specify kind in offering.) (45)
- Destroyed Steel Cars
Bodies
of steel cars cut apart sufficiently to load. (Specify kind.) (45A)
- Destroyed Steel Car Sides And Box Car Roofs.
Cut
to a maximum length of... and a maximum width of... suitable for use in super
presses and shears without additional preparation. Metals
- Ferrous Scrap » Special Boring Grades
267
- No. 1 Chemical Borings
New
clean cast or malleable iron borings and drillings containing not more than 1
percent oil, free from steel turnings, or chips, lumps, scale, corroded or
rusty material. 268
- Briquetted Cast Iron Borings, Hot Process
Cast
iron borings, heated, briquetted, to a density of approximately 85 percent,
oil and water content under 1 percent. 269
- Briquetted Cast Iron Borings, Cold Process
Cast
iron boring briquettes, free of steel and nonferrous material, hydraulically
compressed into a cohesive solid, reasonably free of oil, and having a density
of not less than 60 percent. 270
- Malleable Borings
Clean
malleable iron borings and drillings, free of steel turnings, scale, lumps and
excessive oil. 271
- No. 2 Chemical Borings.
New
clean cast or malleable iron borings and drillings, containing not more than
1.5 percent oil, free from steel turnings, or chips, lumps, scale, corroded or
rusty material. Metals - Ferrous Scrap » Steel From Scrap Tires
272
- Pulled Bead Wire (Truck)—Grade 1.
Not
chopped; made up of loops of wire. Less than five percent (<5%)
rubber/fiber. 273
- Pulled Bead Wire (Truck)—Grade 2
Not
chopped; made up of loops of wire. Five to ten percent (5-10%) rubber/fiber. 274
- Pulled Bead Wire (Truck)—Grade 3
Not
chopped; made up of loops of wire. Greater than ten percent (>10%)
rubber/fiber. 275
- Pulled Bead Wire (Passenger)—Grade 1
Not
chopped; made up of loops of wire. Less than five percent (<5%)
rubber/fiber. 276
- Pulled Bead Wire (Passenger)—Grade 2
Not
chopped; made up of loops of wire. Five to ten percent (5-10%) rubber/fiber. 277
- Pulled Bead Wire (Passenger)—Grade 3
Not
chopped; made up of loops of wire. Greater than ten percent (>10%)
rubber/fiber. 278
- Processed Tire Wire (Ferrous)—Grade 1
Chopped.
Less than two percent (<2%) rubber/fiber. 279
- Processed Tire Wire (Ferrous)—Grade 2
Chopped.
Less than five percent (<5%) rubber/fiber. 280
- Processed Tire Wire (Ferrous)—Grade 3
Chopped.
Five to ten percent (5-10%) rubber/fiber. 281
- Processed Tire Wire (Ferrous)—Grade 4
Chopped.
Ten to twenty percent (10-20%) rubber/ fiber. 282
- Processed Tire Wire (Ferrous)—Grade 5.
Chopped.
Greater than twenty percent (>20%) rubber/ fiber. Metals - Non-Ferrous Scrap
Metals - Non-Ferrous Scrap » Aluminum
Tablet
- Clean Aluminum Lithographic Sheets
To
consist of 1000 and/or 3000 series alloys, to be free of paper, plastic,
excessively inked sheets, and any other contaminants. Minimum size of 3"
(8 cm) in any direction. Tabloid
- New, Clean Aluminum Lithographic Sheets
To
consist of 1000 and/or 3000 series alloys, uncoated, unpainted, to be free of
paper, plastic,ink, and any other contaminants. Minimum size of 3" (8 cm)
in any direction. Taboo
- Mixed Low Copper Aluminum Clippings And Solids
Shall
consist of new, clean, uncoated and unpainted low copper aluminum scrap of two
or more alloys with a minimum thickness of 0.015 inches (.38 mm) and to be
free of 2000 and 7000 series, hair wire, wire screen, punchings less 1/2 inch
(1.25 cm) diameter, dirt, and other non-metallic items. Grease and oil not to
total more than 1%.Variations to this specification should be agreed upon
prior to shipment between the buyer and seller. Taint/Tabor
- Clean Mixed Old Alloy Sheet Aluminum
Shall
consist of clean old alloy aluminum sheet of two or more alloys, free of foil,
venetian blinds, castings, hair wire, screen wire, food or beverage
containers, radiator shells, airplanesheet, bottlecaps, plastic, dirt, and
other non-metallic items. Oil and grease not to total more than 1%. Up to 10%
Tale permitted. Take
- New Aluminum Can Stock
Shall
consist of new low copper aluminum can stock and clippings, clean,
lithographed or not lithographed, and coated with clear lacquer but free of
lids with sealers, iron, dirt and other foreign contamination.Oil not to
exceed 1%. Talc
- Post-Consumer Aluminum Can Scrap
Shall
consist of old aluminum food and/or beverage cans. The material is to be free
of other scrap metals, foil, tin cans, plastic bottles, paper, glass, and
other non-metallic items. Variations to this specification should be agreed
upon prior to shipment between the buyer and seller. Talcred
- Shredded Aluminum Used Beverage Can (Ubc) Scrap
Shall
have a density of 12 to 17 pounds per cubic foot (193 to 273 kg/m3). Material
should contain maximum 5% fines less than 4 mesh (U.S. standard screen size)
(6.35 mm). Must be magnetically separated material and free of steel, lead,
bottle caps, plastic cans and other plastics, glass, wood,dirt, grease, trash,
and other foreign substances. Any free lead is basis for rejection. Any and
all aluminum items, other than used beverage cans, are not
acceptable.Variations to this specification should be agreed upon prior to
shipment between the seller and buyer. Taldack
- Densified Aluminum Used Beverage Can (Ubc) Scrap
Shall
have a biscuit density of 35 to 50 pounds per cubic foot (562 to 802 kg/m3).
Each biscuit not to exceed 60 pounds (27.2 kg). Nominal biscuit size range
from 10" to 13" x 101/4" (25.4 x33 x 26 cm) to 20" x
61/4" x 9" (50.8 x 15.9 x 22.9 cm). Shall have banding slots in both
directions to facilitate bundle banding. All biscuits comprising a bundle must
be of uniform size. Size: Bundle range dimensions acceptable are 41" to
44" x 51" (104 to 112 cm) to 54" x 54" (137 x 137 cm) to
56´(142 cm) high.The only acceptable tying method shall be as follows: Using
minimum 5/8" (1.6cm) wide by .020" (.05 cm) thick steel straps, the
bundles are to be banded with one vertical band per row and a minimum of two
firth (horizontal) bands per bundle. Use of skids and/or support sheets of any
material is not acceptable. Must be magnetically separated material and free
of steel, lead, bottle caps, plastic cans and other plastic, glass, wood,
dirt, grease, trash, and other foreign substances. Any free lead is basis for
rejection.Any and all aluminum items, other than used beverage cans, are not
acceptable. Items not covered in the specifications, including moisture, and
any variations to this specification should be agreed upon prior to shipment
between the seller and buyer. Taldon
- Baled Aluminum Used Beverage Can (Ubc) Scrap
Shall
have a minimum density of 14 pounds per cubic foot (225 kg/m3), and a maximum
density of 17 pounds per cubic foot (273 kg/m3) for unflattened UBC and 22
pounds per cubic foot (353kg/m3) for flattened UBC. Size: Minimum 30 cubic
feet (.85 m3), with bale range dimensions of 24" to 40" (61 to 132
cm) by 30" to 52" (76 to 132 cm) by 40" to 84"(102 to 213
cm). The only acceptable tying method shall be as follows: four to six
5/8" (1.6 cm) x .020" (5 mm) steel bands,or six to ten #13 gauge
steel wires (aluminum bands or wires are acceptable in equivalent strength and
number). Use of skids and/or support sheets of any material is not
acceptable.Must be magnetically separated material and free of steel, lead,
bottle caps, plastic cans and other plastic, glass, wood, dirt, grease, trash,
and other foreign substances. Any free lead is basis for rejection. Any and
all aluminum items, other than used beverage cans, are
notacceptable.Variations to this specification should be agreed upon prior to
shipment between the buyer and seller Taldork
- Briquetued Aluminum Used Beverage Can (Ubc) Scrap
Shall
have a briquette density of 50 pounds per cubic foot (800 kg/m3) minimum.
Nominal briquette size shall range from 12" to 24" (30.5 x 61 cm) x
12" to 24" (30.5 x 61 cm) in uniform profile with a variable length
of 8" (20.3 cm) minimum and 48" (122 cm) maximum. Briquettesshall be
bundled or stacked on skids and secured with a minimum of one vertical band
per rowand a minimum of one girth band per horizontal layer. Briquettes not to
overhang pallet.Total package height shall be 48 (122 cm) maximum.Banding
shall be at least 5/8" (1.6 cm) wide by .020" (5 mm) thick steel
strapping or equivalentstrength.The weight of any bundle shall not exceed
4,000 pounds (1.814 tm). Material must be magnetically separated and free of
steel, plastic, glass, dirt and all other foreign substances. Any and all
aluminum items other than UBC are unacceptable. Any free lead is basis for
rejection. Items not covered in the specification, including moisture,and any
variations to this specification should be agreed upon prior to shipment
between the buyer and seller Tale
- Painted Siding
Shall
consist of clean, low copper aluminum siding scrap, painted one or two sides,
free of plastic coating, iron, dirt, corrosion, fiber, foam, or fiberglass
backing or other non-metallic items. Talk
- Aluminum Copper Radiators
Shall
consist of clean aluminum and copper radiators, and/or aluminum fins on copper
tubing,free of brass tubing, iron and other foreign contamination. Tall
- E.C. Aluminum Nodules
Shall
consist of clean E.C. aluminum, chopped or shredded, free of screening,
hair-wire, iron,copper, insulation and other non-metallic items. Must be free
of minus 20 mesh material. Must contain 99.45% aluminum content. Talon
- New Pure Aluminum Wire And Cable
Shall
consist of new, clean, unalloyed aluminum wire or cable free from hair wire,
ACSR, wire screen, iron, insulation and other nonmetallic items. Tann
- New Mixed Aluminum Wire And Cable
Shall
consist of new, clean unalloyed aluminum wire or cable which may contain up to
10% 6000 series wire and cable free from hair wire, wire screen, iron,
insulation and other non-metallic items. Taste
- Old Pure Aluminum Wire And Cable
Shall
consist of old, unalloyed aluminum wire and cable containing not over 1% free
oxide or dirt and free from hair wire, wire screen, iron, insulation and other
non-metallic items. Tassel
- Old Mixed Aluminum Wire And Cable
Shall
consist of old, unalloyed aluminum wire and cable which may contain up to 10%
6000 series wire and cable with not over 1% free oxide or dirt and free from
hair wire, wire screen,iron, insulation and other non-metallic items. Tarry
A - Clean Aluminum Pistons
Shall
consist of clean aluminum pistons to be free from struts, bushings, shafts,
iron rings and non-metallic items. Oil and grease not to exceed 2% Tarry
B - Clean Aluminum Pistons With Struts
Shall
consist of clean whole aluminum pistons with struts. Material is to be free
from bushings,shafts, iron and non-metallic items . Oil and grease not to
exceed 2%. Tarry
C - Irony Aluminum Pistons
Shall
consist of aluminum pistons with non-aluminum attachments to be sold on a
recovery basis or by special arrangement between buyer and seller. Teens
- Segregated Aluminum Borings And Turnings
Shall
consist of aluminum borings and turnings of one specified alloy. Material
should be free of oxidation, dirt, free iron, stainless steel, magnesium, oil,
flammable liquids, moisture and other non metallic items. Fines should not
exceed 3% through a 20 mesh (U.S. standard) screen. Telic
- Mixed Aluminum Borings And Turnings
Shall
consist of clean, uncorroded aluminum borings and turnings of two or more
alloys and subject to deductions for fines in excess of 3% through a 20 mesh
screen and dirt, free iron, oil,moisture and all other non-metallic items.
Material containing iron in excess of 10% and/or free magnesium or stainless
steel or containing highly flammable cutting compounds will not constitute
good delivery.To avoid dispute, material should be sold on basis of definite
maximum zinc, tin and magnesium content. Tense
- Mixed Aluminum Castings
Shall
consist of all clean aluminum castings which may contain auto and airplane
castings but no ingots, and to be free of iron, brass,dirt and other
non-metallic items. Oil and grease not to total more than 2%. Tepid
- Aircraft Sheet Aluminum
Should
be sold on recovery basis or by special arrangements with purchaser. Terse
- New Aluminum Foil
Shall
consist of clean, new, pure, uncoated 1000 and/or 3000 and/or 8000 series
alloy aluminum foil, free from anodized foil, radar foil and chaff, paper,
plastics, or any other non-metallic items.Hydraulically briquetted material
and other alloys by agreement between buyer and seller. Tesla
- Post Consumer Aluminum Foil
Shall
consist of baled old household aluminum foil and formed foil containers of
uncoated 1000,3000 and 8000 series aluminum alloy. Material may be anodized
and contain a maximum of 5%organic residue. Material must be free from radar
chaff foil, chemically etched foil, laminated foils, iron, paper, plastic and
other nonmetallic contaminants. Tetra
- New Coated Aluminum Foil
Shall
consist of new aluminum foil coated or laminated with ink, lacquers, paper, or
plastic.Material shall be clean, dry, free of loose plastic, PVC and other
non-metallic items. This foil is sold on a metal content basis or by sample as
agreed between buyer and seller. Thigh
- Aluminum Grindings
Should
be sold on recovery basis or by special arrangements with purchaser. Thirl
- Aluminum Drosses, Spatters, Spillings, Skimmings And Sweepings
Should
be sold on recovery basis or by special arrangements with purchaser. Throb
- Sweated Aluminum
Shall
consist of aluminum scrap which has been sweated or melted into a form or
shape such as an ingot, sow or slab for convenience in shipping; to be free
from corrosion, dross or any non-aluminum inclusions. Should be sold subject
to sample or analysis. Tooth
- Segregated New Aluminum Alloy Clippings And Solids
Shall
consist of new, clean, uncoated and unpainted aluminum scrap of one specified
aluminum alloy with a minimum thickness of .015" (.38 mm) and to be free
of hair wire, wire screen, dirt and other non-metallic items. Oil and grease
not to total more than 1%. Also free from punchings less than 1/2" (1.27
cm) in size. Tough
- Mixed New Aluminum Alloy Clippings And Solids
Shall
consist of new, clean, uncoated and unpainted aluminum scrap of two or more
alloys with aminimum thickness of .015" (.38 mm) and to be free of hair
wire, wire screen, dirt and other non metallic items. Oil and grease not to
total more than 1%.Also free from punchings less than 1/2" (1.27 cm) in
size. Tread
- Segregated New Aluminum Castings, Forgings And Extrusions
Shall
consist of new, clean, uncoated aluminum castings, forgings, and extrusions of
one specified alloy only and to be free from sawings, stainless steel, zinc,
iron, dirt, oil, grease and other non metallic items. Troma
- Aluminum Auto Or Truck Wheels
Shall
consist of clean, single-piece, unplated aluminum wheels of a single specified
alloy, free of all inserts, steel, wheel weights, valve stems, tires, grease
and oil and other non-metallic items.Variations to this specification should
be agreed upon prior to shipment between the buyer and seller. Trump
- Aluminum Auto Castings
Shall
consist of all clean automobile aluminum castings of sufficient size to be
readily identified and to be free from iron, dirt, brass, bushings, and
non-metallic items. Oil and grease not to total more than 2%. Twang
- Insulated Aluminum Wire Scrap
Shall
consist of aluminum wire scrap with various types of insulation. To be sold on
a sample or recovery basis, subject to arrangement between buyer and seller. Twist
- Aluminum Airplane Castings
Shall
consist of clean aluminum castings from airplanes and to be free from iron,
dirt, brass, bushings, and non-metallic items. Oil and grease not to total
more than 2%. Twitch
- Fragmentizer Aluminum Scrap (From Automobile Shredders)
The
material, as received, must be dry and not contain more than 3% maximum free
zinc, 1% maximum free magnesium, and 1.5% maximum free iron and stainless. Not
to contain more than a total 5% maximum of non-metallics, of which no more
than 1% shall be rubber and plastics.To be free of excessively oxidized
material, air bag canisters, or any sealed or pressurized items. Any variation
to be sold by special arrangement between buyer and seller. Tally
- All Aluminum Radiators From Automobiles
Shall
consist of clean aluminum radiators and/or condensers. Should be free of all
other types of radiators. All contaminants including iron, plastic, and foam
not to exceed 1% of weight. Any deviation to this specification, including
oxidation and aluminum content, to be negotiated between buyer and seller. Tata
- New Production Aluminum Extrusions
Shall
consist of one alloy (typically 6063). Material may contain “butt ends”
from the extrusion process but must be free of any foreign contamination.
Anodized material is acceptable. Painted material or alloys other than 6063
must be agreed upon by buyer and seller. Toto
- Aluminum Extrusions “10/10”
Material
to consist of new production and old/used 6063 extrusions that may contain up
to (but not exceed) 10 percent painted extrusions and 10 percent 6061 alloy
extrusions. Must not contain other alloys of aluminum. Material should be free
of zinc corners, iron attachments, felt, plastic, paper, cardboard, thermo
break, and dirt and other contaminants. Tutu
- Aluminum Extrusion Dealer Grade
Shall
consist of old extruded aluminum of one alloy, typically alloy 6063, 6061, or
7075. Material must be free of iron, thermo break, saw chips, zinc corners,
dirt, paper, cardboard, and other foreign contamination. Percentages of paint
or other alloys to be agreed upon by buyer and seller. Tweak
- Fragmentizer Aluminum Scrap (From Automobile Shredders)
Derived
from either mechanical or hand separation, the material must be dry and not
contain more than 4% maximum free zinc, 1% maximum free magnesium, and 1.5%
maximum of analytical iron. Not to contain more than a total 5% maximum of
nonmetallics, of which no more than 1% shall be rubber and plastics. To be
free of excessively oxidized material, air bag canisters, or any sealed or
pressurized items. Any variation to be sold by special arrangement between
buyer and seller. Twire
- Burnt Fragmentizer Aluminum Scrap (From Automobile Shredders)
Incinerated
or burned material must be dry and not contain more than X% (% to be agreed
upon by buyer and seller) ash from incineration, 4% maximum free zinc, 1%
maximum free magnesium, and 1.5% maximum of analytical iron. Not to contain
more than a total 5% maximum of non-metallics, of which no more than 1% shall
be rubber and plastics. To be free of excessively oxidized material, air bag
canisters, or any sealed pressurized items. Any variation to be sold by
special arrangement between buyer and seller. Metals
- Non-Ferrous Scrap » Mixed Metals
Zorba
- Shredded Nonferrous Scrap (Predominantly Aluminum)
Shall
be made up of a combination of the nonferrous metals: aluminum, copper, lead,
magnesium, stainless steel, nickel, tin, and zinc, in elemental or alloyed
(solid) form. The percentage of each metal within the nonferrous concentrate
shall be subject to agreement between buyer and seller. Material generated by
eddy current, air separation, flotation, screening, other segregation
technique(s), or a combination thereof. Shall have passed one or more magnets
to reduce or eliminate free iron and/or large iron attachments. Shall be free
of radioactive material, dross, or ash. Material to be bought/sold under this
guideline shall be identified as “Zorba” with a number to follow
indicating the estimated percentage nonferrous metal content of the material
(e.g., “Zorba 90” means the material contains approximately 90% nonferrous
metal content). May also be screened to permit description by specific size
ranges. Zebra
- (High Density)
Shall
consist of high-density nonferrous metals produced by media separation
technology containing brass, copper, zinc, nonmagnetic stainless steel, and
copper wire. Material to be dry and free from excess oxidation. The percentage
and types of metals other than these, as well as the percentage and types of
nonmetallic contamination are to be agreed upon between the buyer and seller. Zeppelin
- (Light Density)
Shall
consist of light-density nonferrous metals produced by media separation
technology and contain thin-gauge aluminum and magnesium. Material to be dry
and free from excess oxidation.The percentage and types of metals other than
aluminum and magnesium, as well as the percentage and types of nonmetallic
contamination are to be agreed upon between the buyer and seller. Elmo
- Mixed Electric Motors
Shall
consist of whole electric motors and/or dismantled electric motor parts that
are primarily copper- wound. May contain aluminum-wound material, subject to
agreement between buyer and seller. No excessive steel attachments such as
gear reducers, iron bases, and pumps, or loose free iron allowed.
Specification not to include sealed units or cast iron compressors. Shelmo
- Shredded Electric Motors
Also
called “shredder pickings” or “meatballs”. Shall consist of mixed
copper-bearing material from ferrous shredding, comprised of motors without
cases. May contain aluminum-wound material and insulated copper harness wire,
subject to agreement between buyer and seller. Trace percentages of other
contaminants and fines may be present. No free iron or sealed units. Zurik
- Shredded Nonferrous Sensor Sorted Scrap (Predominantly Stainless Steel)
Shall
be made up of a combination of the nonferrous metals: stainless steel,
insulated copper wire, aluminum, copper, lead, magnesium, nickel, tin, and
zinc, in elemental or alloyed (solid) form. The percentage of each metal
within the nonferrous concentrate shall be subject to agreement between buyer
and seller. Material generated by computer sensing equipment (e.g., induction
sensor sorting or X-ray) technique(s). Shall have passed one or more magnets
to reduce or eliminate free iron and/or large iron attachments. Shall be free
of radioactive material, dross, or ash. Material to be bought/sold under this
guideline shall be identified as “Zurik” with a number to follow
indicating the estimated percentage nonferrous content of the material (e.g.,
“Zurik 90” means the material contains approximately 90% nonferrous metal
content). May also be screened to permit description by specific size ranges. Metals
- Non-Ferrous Scrap » Nickel/Stainless/Hi Temp
Aroma
- New Nickel Scrap
Shall
consist of clean new sheet, plate, bar, tube, and any other wrought nickel
scrap solids. Nickel minimum 99%; Cobalt maximum 0.25%; Copper maximum 0.50%.
Free of castings, as well as any foreign attachments or other contamination. Burly
- Old Nickel Scrap
Shall
consist of old and/or new sheet, plate, bar, tube, and any other wrought
nickel scrap solids. Material to contain a minimum of 98% nickel; Copper
maximum 0.50%.This grade to be free of castings,soldered, brazed, sweated, or
painted material, other metallic coating, foreign attachments, and any other
contamination. Dandy
- New Cupro Nickel Clips And Solids
Shall
consist of clean, new, segregated (normally accepted analysis grades) either
70/30, 80/20,or 90/10 cupro nickel tube, pipe, sheet, plate, or other wrought
solid forms. Must be free of foreign attachments or any other contamination. Daunt
- Cupro Nickel Solids
Shall
consist of old, and/or new, segregated (normally accepted analysis grades
either 70/30,80/20, 90/10 cupro nickel tube, pipe, sheet, plate, or other
wrought solid forms. Maximum 2% sediment allowable. Any other forms of cupro
nickel solids such as castings, gates, risers, spills, etc., packaged
separately, may or may not be included, only upon agreement between buyer and
seller. Must be free of foreign attachments and all other contamination. Other
particulars concerning physical description, analysis and packaging to be
agreed upon between buyer and seller. Delta
- Soldered Cupro Nickel Solids
Shall
consist of segregated (normally accepted analysis grades) either 70/30, 80/20,
90/10 cupro nickel solids, soldered, brazed, or sweated, must be free of
trimmed seams and edges and all other contamination. Decoy
- Curpo Nickel Spinnings,Turnings, Borings
Shall
consist of clean segregated (normally accepted analysis grades) either 70/30,
80/20, 90/10 cupro nickel spinnings, turnings, or borings. Particulars
concerning physical description,analysis, packaging, to be agreed upon between
buyer and seller. Depth
- Miscellaneous Nickel-Copper And Nickel-Copper Iron
Shall
consist of miscellaneous scrap in which the basic elements, by weight, are
nickel and copper, such as copper nickel peelings, plating racks, and hangers,
and all nickel and copper in attached or combined form. In all cases,
miscellaneous nickel copper scrap should be sold by description and analysis. Hitch
- New R-Monel Clippings And Solids
Shall
consist of clean, new, R-Monel sheet, plate, bar, rod, tube, pipe, or any
other wrought scrap, free of any foreign attachments or any other
contamination. House
- New Mixed Monel Solids And Clippings
Shall
consist of new, clean R and K-Monel solids and clippings. Free of cast
material, foreign attachments and all other contamination. Ideal
- Old Monel Sheet And Solids
Shall
consist of clean R and K-Monel solids such as sheet, plate, pipe, rods,
forgings, screen and wire cloth. Must be free of soldered, brazed, welded, or
sweated material, cast material, foreign attachments, and all other
contamination. Indian
- K-Monel Solids
Shall
consist of clean K-Monel solids Junto
- Soldered Monel Sheet And Solids
Shall
consist of soldered and/or brazed miscellaneous grades of Monel alloys in
either wrought or cast form. Must be free of trimmed seams and edges,
non-metallic filling, foreign attachments, and all other contamination.
Particulars concerning physical description, assay, and packaging to be agreed
upon between buyer and seller. Lemon
- Monel Castings
Shall
consist of various types of clean Monel castings, assaying minimum 60% nickel.
Must be free of foreign attachments or any other contamination. Lemur
- Monel Turnings
Shall
consist of mixed Monel turnings and borings containing a minimum of 60% nickel
content,on a dry basis. Pekoe
- 200 Series Stainless Steel Scrap Solids
Shall
consist of all types of clean AISI Series Stainless Steel Scrap Solids, which
contain a maximum of .5% copper, free of foreign attachments and other
contamination. Sabot
- Stainless Steel Scrap
Shall
consist of clean 18-8 type stainless steel clips and solids containing a
minimum 7% nickel,16% chrome, and have a maximum of .50% molybdenum, .50%
copper, .045% phosphorous,and.03% sulfur, and otherwise free of harmful
contaminants. Particulars concerning physical description, grading, additional
analysis, and preparation to be agreed upon between buyer and seller. Ultra
- Stainless Steel Turnings
Shall
consist of clean 18-8 type stainless steel turnings containing a minimum 7%
nickel and 16% chrome, and to be free of nonferrous metals, non metallics,
excessive iron, oil and other contaminants.Particulars concerning physical
description, assay, packaging to be agreed upon between buyer and seller. Vaunt
- Edison Batteries
Nickel-iron
batteries to be sold free of crates, copper terminal connectors, and excess
liquid. Free of nickel cadmium batteries. Metals - Non-Ferrous Scrap » Other
Ranks
- Pewter
Shall
consist of tableware and soda-fountain boxes but should contain a minimum of
84% tin.Siphon tops to be accounted for separately.Material must be free of
brass, zinc, and other foreign metals. Ranch
- Block Tin
Block
Tin must assay minimum of 98% tin, and to be free of liquids, solder, and
brass connections, pewter, pumps, pot pieces, dirt. Raves
- High Tin Base Babbitt
Shall
contain a minimum of 78% tin and be free of brassy or zincy metals. Roses
- Mixed Common Babbitt
Shall
consist of lead base bearing metal containing not less than 8% tin, free from
Allens metal, ornamental, antimonial and type metal. Must be free from all
zinc and excessive copper in the alloy. Metals - Non-Ferrous Scrap » Red Metals
Barley
- No. 1 Copper Wire
Shall
consist of No. 1 bare, uncoated, unalloyed copper wire, not smaller than No.
16 B & S wiregauge. Green copper wire and hydraulically compacted material
to be subject to agreement between buyer and seller. Berry
- No. 1 Copper Wire
Shall
consist of clean, untinned, uncoated, unalloyed copper wire and cable, not
smaller than No.16 B & S wire gauge, free of burntwire which is brittle.
Hydraulically briquetted copper subject to agreement. Birch
- No. 2 Copper Wire
Shall
consist of miscellaneous, unalloyed copper wire having a nominal 96% copper
content(minimum 94%) as determined by electrolytic assay. Should be free of
the following.Excessively leaded, tinned, soldered copper wire; brass and
bronze wire; excessive oil content, iron, and non-metallics; copper wire from
burning, containing insulation; hair wire; burnt wire which is brittle; and
should be reasonably free of ash. Hydraulically briquetted copper subject to
agreement. Candy
- No. 1 Heavy Copper
Shall
consist of clean, unalloyed, uncoated copper clippings, punchings, bus bars,
commutator segments, and wire not less than 1/16 of an inch thick, free of
burnt wire which is brittle; but may include clean copper tubing.
Hydraulically briquetted copper subject to agreement. Cliff
- No. 2 Copper
Shall
consist of miscellaneous, unalloyed copper scrap having a nominal 96% copper
content(minimum 94%) as determined by electrolytic assay. Should be free of
the following: Excessively leaded, tinned, soldered copper scrap; brasses and
bronzes; excessive oil content, iron and non-metallics; copper tubing with
other than copper connections or with sediment; copper wire from burning,
containing insulation; hair wire; burnt wire which is brittle; and should be
reasonably free of ash.Hydraulically briquetted copper subject to agreement. Clove
- No. 1 Copper Wire Nodules
Shall
consist of No. 1 bare, uncoated, unalloyed copper wire scrap nodules, chopped
or shredded,free of tin, lead, zinc, aluminum,iron, other metallic impurities,
insulation, and other foreign contamination. Minimum copper 99%. Gauge smaller
than No. 16 B & S wire and hydraulically compacted material subject to
agreement between buyer and seller. Cobra
- No. 2 Copper Wire Nodules
Shall
consist of No. 2 unalloyed copper wire scrap nodules, chopped or shredded,
minimum 97%copper. Maximum metal impurities not to exceed 0.50% aluminum and
1% each of other metals or insulation. Hydraulically compacted material
subject to agreement between buyer and seller. Cocoa
- Copper Wire Nodules
Shall
consist of unalloyed copper wire scrap nodules, chopped or shredded, minimum
99%copper. Shall be free of excessive insulation and other non-metallics.
Maximum metal impurities as follows: Aluminum - .05% Tin - .25% Nickel - .05%
Antimony - .01% Iron - .05% Hydraulically compacted material subject to
agreement between buyer and seller. Dream
- Light Copper
Shall
consist of miscellaneous, unalloyed copper scrap having a nominal 92% copper
content(minimum 88%) as determined by electrolytic assay and shall consist of
sheet copper, gutters, downspouts, kettles, boilers, and similar scrap. Should
be free of the following: Burnt hair wire; copper clad; plating racks;
grindings; copper wire from burning, containing insulation; radiators, fire
extinguishers;refrigerator units; electrotype shells; screening; excessively
leaded, tinned, soldered scrap; brasses and bronzes; excessive oil, iron and
non-metallics; and should be reasonably free of ash. Hydraulically briquetted
cop-per subject to agreement. Any items excluded in this grade are also
excluded in the higher grades above Drink
- Refinery Brass
Shall
contain a minimum of 61.3% copper and maximum 5% iron and to consist of brass
and bronze solids and turnings, and alloyed and contaminated copper scrap.
Shall be free of insulated wire, grindings, electrotype shells and
non-metallics. Hydraulically briquetted material subject to agreement. Drove
- Copper-Bearing Scrap
Shall
consist of miscellaneous copper-containing skimmings, grindings, ashes, irony
brass and copper, residues and slags. Free of insulated wires; copper
chlorides; unprepared tangled material; large motors; pyrophoric material;
asbestos brake linings; furnace bottoms; high lead materials; graphite
crucibles; and noxious and explosive materials. Fine powdered material by
agreement. Hydraulically briquetted material subject to agreement. Druid
- Insulated Copper Wire Scrap
Shall
consist of copper wire scrap with various types of insulation. To be sold on a
sample or recovery basis, subject to agreement between buyer and seller Ebony
- Composition Or Red Brass
Shall
consist of red brass scrap, valves, machinery bearings and other machinery
parts, including miscellaneous castings made of copper, tin, zinc, and/or
lead. Should be free of semi-red brass castings (78% to 81% copper); railroad
car boxes and other similar high-lead alloys; cocks and faucets; closed water
meters; gates; pot pieces; ingots and burned brass; aluminum, silicon, and
manganese bronzes; iron and non-metallics. No piece to measure more than
12" over any one part or weigh over 100 lbs. Enerv
- Red Brass Composition Turnings
Shall
consist of turnings from red brass composition material and should be sold
subject to sample or analysis. Elder
- Genuine Babbitt-Lined Brass Bushings
Shall
consist of red brass bushings and bearings from automobiles and other
machinery, shall contain not less than 12% high tin-base babbitt, and shall be
free of iron-backed bearings. Elias
- High Lead Bronze Solids And Borings
It
is recommended that these materials be sold on sample or analysis Engel
- Machinery Or Hard Brass Solids
Shall
have a copper content of not less than 75%, a tin content of not less than 6%,
and a lead content of not less than 6% - nor more than 11%, and total
impurities, exclusive of zinc,antimony, and nickel of not more than 0.75%; the
antimony content not to exceed 0.50%. Shall be free of lined and unlined
standard red car boxes. Erin
- Machinery Or Hard Brass Borings
Shall
have a copper content of not less than 75%, a tin content of not less than 6%,
and a leadcontent of not less than 6%²nor more than 11%, and the total
impurities, exclusive of zinc,antimony, and nickel of not more than 0.75%, the
antimony content not to exceed 0.50%. Fence
- Unlined Standard Red Car Boxes (Clean Journals)
Shall
consist of standard unlined and/or sweated railroad boxes and unlined and/or
sweated car journal bearings, free of yellow boxes and iron-backed boxes. Ferry
- Lined Standard Red Car Boxes (Lined Journals)
Shall
consist of standard babbitt-lined railroad boxes and/or babbitt- lined car
journal bearings, free of yellow boxes and iron-backed boxes. Grape
- Cocks And Faucets
Shall
consist of mixed clean red and yellow brass, including chrome or
nickel-plated, free of gas cocks, beer faucets, and aluminum and zinc base die
cast material, and to contain a minimum of 35% semi-red. Honey
- Yellow Brass Scrap
Shall
consist of brass castings, rolled brass, rod brass, tubing and miscellaneous
yellow brasses, including plated brass. Must be free of manganese-bronze,
aluminum-bronze, unsweated radiators or radiator parts, iron, excessively
dirty and corroded materials. Ivory
- Yellow Brass Castings
Shall
consist of yellow brass castings in crucible shape, no piece to measure more
than 12 inches over any one part; and shall be free of brass forgings, silicon
bronze, aluminum bronze and manganese bronze, and not to contain more than 15%
nickel plated material. Label
- New Brass Clippings
Shall
consist of the cuttings of new unleaded yellow brass sheet or plate, to be
clean and free from foreign substances and not to contain more than 10% of
clean brass punchings under ¼inch.To be free of Muntz metal and naval brass. Lace
- Brass Shell Cases Without Primers
Shall
consist of clean fired 70/30 brass shell cases free of primers and any other
foreign material. Lady
- Brass Shell Cases With Primers
Shall
consist of clean fired 70/30 brass shell cases containing the brass primers
and which contain no other foreign material. Lake
- Brass Small Arms And Rifle Shells, Clean Fired
Shall
consist of clean fired 70/30 brass shells free of bullets, iron and any other
foreign material. Lamb
- Brass Small Arms And Rifle Shells, Clean Muffled (Popped)
Lark
- Yellow Brass Primer
Shall
consist of clean yellow brass primers, burnt or unburnt. Free of iron,
excessive dirt, corrosion and any other foreign material. Maize
- Mixed New Nickel Silver Clippings
Shall
consist of one or more nickel silver alloys and the range of nickel content to
be specified,free of chrome or any other plating material. Leaded nickel
silver clippings should be packed and sold separately. Not to contain more
than 10% of clean punchings under ¼ inch. Major
- New Nickel Silver Clippings And Solids
Shall
consist of new, clean nickel silver clippings, plate, rod and forgings, and
other rolled shapes, free of chrome or any other plating material. Must be
sold on nickel content specifications such as 10%±12%±15%±18%±20%. Leaded
nickel silver clippings should be packed and sold separately. A description as
to its physical characteristics should be made in offering all nickel silver
material. Malar
- New Segregated Nickel Silver Clippings
Shall
consist of one specified nickel silver alloy. Not to contain more than 10% of
clean punchings under ¼ inch. Malic
- Old Nickel Silver
Shall
consist of old nickel silver sheet, pipe, rod, tubes, wire, screen, soldered
or unsoldered. Must not be trimmed seams alone and it is also to be free of
foreign substances, iron rimmed material and other metals. Melon
- Brass Pipe
Shall
consist of brass pipe free of plated and soldered materials or pipes with cast
brass connections.To be sound, clean pipes free of sediment and condenser
tubes. Naggy
- Nickel Silver Castings
To
be packed and sold separately. Niece
- Nickel Silver Turnings
To
be sold by sample or analysis. Night
- Yellow Brass Rod Turnings
Shall
consist of strictly rod turnings, free of aluminum, manganese, composition,
Tobin and Muntz metal turnings; not to contain over 3% free iron, oil or other
moisture; to be free of grindings and babbitts;to contain not more than 0.30%
tin and not more than 0.15% alloyed iron. Noble
- New Yellow Brass Rod Ends
Shall
consist of new, clean rod ends from free turning brass rods or forging rods,
not to contain more than 0.30% tin and not more than 0.15% alloyed iron. To be
free of Muntz metal and naval brass or any other alloys.To be in pieces not
larger than 12" and free of foreign matter. Nomad
- Yellow Brass Turnings
Shall
consist of yellow brass turnings, free of aluminum, manganese and composition
turnings,not to contain over 3% of free iron, oil or other moisture; to be
free of grindings and babbitts. To avoid dispute, to be sold subject to sample
or analysis. Ocean
- Mixed Unsweated Auto Radiators
Shall
consist of mixed automobile radiators, to be free of aluminum radiators, and
iron finned radiators. All radiators to be subject to deduction of actual
iron. The tonnage specification should cover the gross weight of the
radiators, unless otherwise specified. Pales
- Admiralty Brass Condenser Tubes
Shall
consist of clean sound Admiralty condenser tubing which may be plated or
un-plated, free of nickel alloy, aluminum alloy, and corroded material. Pallu
- Aluminum Brass Condenser Tubes
Shall
consist of clean sound condenser tubing which may be plated or unplated, free
of nickel alloy and corroded material. Palms
- Muntz Metal Tubes
Shall
consist of clean sound Muntz metal tubing which may be plated or unplated,
free of nickel alloy, aluminum alloy, and corroded material. Parch
- Manganese Bronze Solids
Shall
have a copper content of not less than 55%, a lead content of not more than
1%, and shall be free of aluminum bronze and silicon bronze. Metals
- Non-Ferrous Scrap » Scrap Lead
Eland
- High Grade-Low Lead Bronze Solids
It
is recommended these materials be sold by analysis. Racks
- Scrap Lead - Soft
Shall
consist of clean soft scrap lead, free of other materials such as drosses,
battery plates, lead covered cable, hard lead, collapsible tubes, foil, type
metals, aluminum, zinc, iron and brass fittings,dirty chemical lead and
radioactive materials. Review packaging specifications and regulatory status
pertaining to shipping with buyer prior to sale. Radio
- Mixed Hard/Soft Scrap Lead
Shall
consist of clean lead solids, free of other materials, such as drosses,
battery plates, lead covered cable, collapsible tubes, type metals, aluminum,
zinc, iron and brass fittings, dirty chemical lead and radioactive materials.
Review packaging specifications and regulatory status pertaining to shipping
with buyer prior to sale. Rails
- Lead Battery Plates
Specify
whether automotive, industrial or mixed. Also whether they are groups or
loose. The only other metallic that might be included could be lead
connectors.To be free of non-metallics,i.e., plastic or rubber, with the
exception that separators may be included. Material to be dry. May be bought
on an assay basis or a flat price. Submarine plates subject to negotiation.
Review packaging specifications and regulatory status pertaining to shipping
with buyer prior to sale. Rains
- Scrap Drained/Dry Whole Intact Lead
To
be free of any liquid. Cases to be either plastic or rubber and be complete
including caps. Non-lead (nicad, ni-fe, carbonaire, etc.) not acceptable.
Industrial, steel cased, aircraft (aluminum cased) and partial, cracked or
broken batteries and batteries without caps subject to special agreement.
Review packaging specifications and regulatory status pertaining to shipping
with buyer prior to sale. Rakes
- Battery Lugs
To
be free of scrap lead, wheel weights, battery plates, rubber and/or plastic
case material and other foreign material. A minimum of 97% metallic content is
required. Review packaging specifications and regulatory status pertaining to
shipping with buyer prior to sale. Relay
- Lead Covered Copper Cable
Free
of armored covered cable, and foreign material. Rents
- Lead Dross
Should
be clean and reasonably free of other materials such as iron, dirt, harmful
chemicals or other metals.To be free of radioactive materials, aluminum and
zinc. May be bought on an assay basis or as agreed to by buyer and seller.
Other metals present such as antimony, tin, etc., to be accounted for as
agreed between buyer and seller. Material to be readily dumped from drums.
Anextra charge may be assessed if material has to be mechanically removed.
Review packaging specification and regulatory status pertaining to shipping
with buyer prior to sale. Rink
- Scrap Wet Whole Intact Lead Batteries
Consisting
of SLI (starting, lighting & ignition), automotive, truck, 8- D and
commercial golf cart and marine-type batteries. Cases to be either plastic or
rubber and to be complete. Non-lead(i.e., ni-cad,ni-fe, carbonaire, etc.) not
acceptable. Other types i.e. aircraft (aluminum) gel-cel, lawnmower, etc., and
partial, cracked or broken batteries or batteries without caps and the amount
of liquid content and any variations to the specification subject to special
agreement. Review packaging specifications and regulatory status pertaining to
shipping with buyer prior to sale. Rono
- Scrap Industrial Intact Lead Cells
Consisting
of plates enclosed by some form of complete plastic case. Partial, cracked or
broken cells, cells without caps and the amount of liquid content and any
variations to the specification subject to special agreement. Review packaging
specifications and regulatory status pertaining to shipping with buyer prior
to sale. Roper
- Scrap Whole Intact Industrial Lead Batteries
Consisting
of bus, diesel, locomotive, telephone and/or steel cased batteries. Submarine
batteries subject to negotiation. Partial,cracked, broken or batteries without
caps and the amount of liquidcontent and any variations to the specification
subject to special agreement. Review packaging specifications and regulatory
status pertaining to shipping with buyer prior to sale Ropes
- Wheel Weights
To
consist of lead tire balances with or without iron clips. Not to include scrap
lead, lugs or plates unless specifically agreed to.To be free of foreign
material. Review packaging specifications and regulatory status pertaining to
shipping with buyer prior to sale. Metals - Non-Ferrous Scrap » Scrap Magnesium
Wafer
- Magnesium Clips
Shall
consist of clean magnesium clips in crucible size, free of copper, aluminum,
and zinc flashings and excessive oil and grease. To be free of all foreign
attachments. Walnut
- Magnesium Scrap
Shall
consist of magnesium castings, magnesium engine blocks and transmission
casings, bomber and car wheels, extrusions, and sheet. Material to be free
from brass and copper inserts and all foreign attachments. To be free of
anodes, hollow castings and explosives. Percentages of and penalties for dirt,
oil, grease, and iron to be subject to agreement between buyer and seller.
Excessively large pieces to be negotiated between buyer and seller. Wine
- Magnesium Engraver Plates
To
be free of copper, aluminum, zinc, and electrotype plates.To be clean and free
of all foreign attachments. Magnesium plates shipped loose by agreement
between buyer and seller. Wood
- Magnesium Dockboards
Shall
consist of clean magnesium dockboard cut or broken to size agreed upon by
buyer and seller. To be free of all foreign attachments. World
- Magnesium Turnings
It
is recommended that these materials be sold by special arrangement between
buyer and seller. Metals - Non-Ferrous Scrap » Scrap Zinc
Saves
- Old Zinc Die Cast Scrap
Shall
consist of miscellaneous old zinc base die castings, with or without iron and
other foreign attachments.Must be free of borings, turnings, dross pieces,
chunks, melted pieces ands kimmings. All unmeltables, dirt, foreign
attachments, and volatile substances (such as rubber, cork, plastic,grease,
etc.) are deductible. Material containing in excess of 30% iron will not
constitute good delivery. Scabs
- New Zinc Die Cast Scrap
Shall
consist of new or unused, clean, zinc base die castings. Castings to be
unplated, unpainted, and free from corrosion. Scope
- New Plated Zinc Die Cast Scrap
Shall
consist of new or unused clean, plated zinc base die castings, free from
corrosion. Scoot
- Zinc Die Cast Automotive Grilles
Shall
consist of clean, old or used zinc base die cast automotive grilles, free from
soldered material. All foreign attachments and extraneous materials are
deductible. Score
- Old Scrap Zinc
Shall
consist of clean dry scrap zinc, such as sheets, jar lids, clean unalloyed
castings and anti-corrosion plates. Borings and turnings are not acceptable.
Material must not be excessively corroded or oxidized. All foreign attachments
and extraneous materials are deductible. Screen
- New Zinc Clippings
Shall
consist of any new pure zinc sheets or stampings free from corrosion. To
contain no foreign material or attachments. Printers zinc, such as engravers
zinc, lithograph sheets and addressograph plates subject to special
arrangements. Printers zinc to be free of routings. Scull
- Zinc Die Cast Slabs Or Pigs
Shall
consist of melted zinc base die cast materials, in smooth clean solid slabs or
pigs. Material to be free from drosses and to contain a minimum zinc content
of 90%.To contain a maximum of 0.1% nickel and maximum of 1% lead. Blocks are
acceptable upon mutual agreement. Scribe
- Crushed Clean Sorted Fragmentizers Die Cast Scrap, As Produced From
Automobile Fragmentizers
To
be clean, free of dirt, oil, glass, rubber, and trash. To contain a maximum of
5% unmeltables such as free iron, copper, aluminum and other metals. Scroll
- Unsorted Zinc Die Cast Scrap
Produced
from automobile fragmentizers. Material to contain about 55% zinc-bearing
scrap.Other nonferrous metals such as aluminum, stainless steel, red metal,
etc., to be about 40%.Insulated copper wire about 1%.Trash, dirt, glass,
rubber, oil, iron, not to exceed 5%. Any variations to be sold by special
arrangement between buyer and seller. Scrub
- Hot Dip Galvanizers Slab Zinc Dross (Batch Process)
Shall
consist only of galvanizers unsweated zinc dross in slab form from hot dip
galvanizing(Batch Process) with a minimum zinc content of 92% and shall be
free of skimmings and trampiron. Broken pieces under 2" in diameter shall
not exceed 10% of the weight of each shipment. Slabs shall not weigh over 100
pounds each. Heavier pieces acceptable upon mutual agreement between buyer and
seller. Material from continuous galvanizing operation is not
acceptable.Blocks are acceptable upon mutual agreement. Seal
- Continuous Line Galvanizing Slab Zinc Top Dross
Shall
consist of unsweated zinc dross removed from the top of a continuous line
galvanizing bath, in slab form not weighing in excess of 100 pounds each, with
a minimum zinc content of 90% Heavier pieces acceptable upon mutual agreement
between buyer and seller. Shall be free of skimmings. Broken pieces under
2" in diameter shall not exceed 10% of the weight of each shipment. Seam
- Continuous Line Galvanizing Slab Zinc Bottom Dross
Shall
consist of unsweated zinc dross removed from the bottom of a continuous line
galvanizing bath, in slab form not weighing in excess of 100 pounds each, with
a minimum zinc content of 92%. Heavier pieces acceptable upon mutual agreement
between buyer and seller. Shall be free of skimmings. Broken pieces under
2" in diameter shall not exceed 10% of the weight of each shipment. Shelf
- Prime Zinc Die Cast Dross
Shall
consist of metal skimmed from the top of pot of molten zinc die cast metal.
Must be unsweated, unfluxed, shiny, smooth, metallic and free from corrosion
or oxidation. Should be poured in molds or in small mounds weighing not over
75 pounds each. Zinc shall be minimum
of 85%. Down load a copy in
pdf |
||
Copyright 2003 - 2020 Iberian Tradelink - All rights reserved. Privacy Policy |